Johannes Bitzer, Christoph Göbel, Ayas Muhamad Ismail, Qi Fu, Martin Muhler, Wolfgang Kleist

• Using the mixed-metal approach, a direct synthesis route at ambient pressure was developed for a new type of bimetallic metal-organic framework based on the CPO-27 structure. The structural characterization of CPO-27(Cu0.6−CS−Co0.4) using X-ray diffraction, transmission electron microscopy, energy-dispersive X-ray mapping and X-ray absorption spectroscopy revealed that the Cu2+ and Co2+ ions were exclusively incorporated at the metal positions of the CPO-27 lattice, but with a core-shell distribution within the crystallites. The parent framework material was then utilized as a precursor for the generation of novel bimetallic carbon-supported materials using the controlled thermal decomposition in a reducing atmosphere. During this decomposition process, the distribution of the two metals remained the same, which resulted in unique needle-shaped particles with a high dispersion of cobalt at the periphery of the amorphous carbon and agglomerated copper particles in the inside.